Aisi type h13 hot work tool steel air or oil quenched from 995 1025 c.
H13 tool steel yield strength.
Lc h13 samples were metallurgically sound and free of cracks or porosity.
H13 tool steel is chromium hot work tool steels which are widely used in hot and cold work tooling applications.
Tensile yield strengths and ductilities for some of the plain carbon and low alloy steels are given in the following mechanical properties of steel chart.
H13 is a hot work tool steel that has good resistance to thermal fatigue erosion and wear and is widely used for making molds and dies.
Uns t20813 astm a681 fed qq t 570 bs 4659 bh13 bs 4659 h13 bs en iso 4957 2000 x40crmov5 1 werkstoff 1 2344.
The hot hardness hot strength of h13 resists thermal fatigue cracking which occurs as a result of cyclic heating and cooling cycles in hot work tooling applications.
Cincinnati tool steel company phone.
Chromium hot work tool steels are designated as group h steels according to the aisi classification system.
This series of steels start from h1 to h19.
H13 tool steel is air hardening hot work 5 chrome tool steel.
815 226 4388 aisi h13 hot work steel h13 combines good red hardness and abrasion resistance with the ability to resist heat checking.
H13 tool steel is classified as group h steels by the aisi classification system.
Most commonly used in plastic molds and die casting its ability to withstand rapid cooling from high working temperatures also make it a prime choice.
H13 tool steel is a versatile chromium molybdenum hot work steel that is widely used in hot work and cold work tooling applications.
H13 tool steel material datasheet typical mechanical properties standard markforged as sintered markforged heat treated wrought heat treated ultimate tensile strength astm e8 1420 mpa 1500 mpa 1580 mpa 0 2 yield strength astm e8 800 mpa 1250 mpa 1360 mpa elongation at break astm e8 5 5 14 hardness astm e18 40 hrc 45 hrc 46 hrc relative.
Yield strength tensile strength and ductility values for steels at room temperature.
Aisi h 13 tool steel is characterized by.
It combines excellent shock and abrasion resistance with good red hardness making it ideal for use in die casting.
It is an aisi h13 hot work tool steel the most widely used steel for aluminum and zinc die casting dies.
Good resistance to abrasion at both.
Able to maintain good strength and wear resistance in high temperatures h13 tool steel also resists cracking from repeated heating and cooling cycles.
It s an air hardening material that s widely used in die casting applications.
This series of steels start from h1 to h19.
The most commonly used chromium hot work steels are h11 h12 and h13 which can be air hardened in 150 mm thick sections.